Question:
Three melt-spun fibre samples A, B and C produced from same polymer under different conditions are found to have densities 1.10 g/cm3, 1.15 g/cm3 and 1.20 g/cm3, respectively. If the mass fraction based degree of crystallinity (xc) of A and C is 0.45 and 0.75, respectively, then xc for B (rounded off to 2 decimal places) is___
Three melt-spun fibre samples A, B and C produced from same polymer under different conditions are found to have densities 1.10 g/cm3, 1.15 g/cm3 and 1.20 g/cm3, respectively. If the mass fraction based degree of crystallinity (xc) of A and C is 0.45 and 0.75, respectively, then xc for B (rounded off to 2 decimal places) is___
Updated On: Jul 27, 2024
Hide Solution
Verified By Collegedunia
Correct Answer: 0.59
Solution and Explanation
The correct Answe is: 0.59 or 0.63 Approx
Was this answer helpful?
0
1
Top Questions on Polymerization methods
- Poly(ethylene terephthalate) has a number average molecular weight of 25000. The degree of polymerisation (rounded off to the nearest integer) is ____
- GATE TF - 2024
- Textile Engineering and Fibre Science
- Polymerization methods
- Amongst the following fibre forming polymers, the one which is synthesised by chain growth polymerisation is
- GATE TF - 2024
- Textile Engineering and Fibre Science
- Polymerization methods
Questions Asked in GATE TF exam
- The value of the integral \( \int_{0}^{\infty} \frac{dx}{e^x + e^{-x}} \) is:
- GATE TF - 2024
- Definite and indefinite integrals
- A winder operates at 750 m/min with 93% efficiency. The time (in minutes) taken for the winder to wind 1.2 kg of 20 tex yarn is approximately _______.
- GATE TF - 2024
- Yarn Manufacture, Structure and Properties
- The approximate value of the integral \( \int_{2}^{3} \frac{dx}{x} \) using Simpson's rule with \( h = 0.5 \) is
- GATE TF - 2024
- Definite and indefinite integrals
- A circular weft knitting machine with 24 inch gauge and 20 inch diameter needle bed is used to make a tubular knitted fabric. If the fabric shrinks by 35% in course- wise direction upon withdrawal from the machine, the circumference (inch) of the shrunk tubular fabric is approximately
- GATE TF - 2024
- Principles of warp knitting
- As the package builds up in a roving frame, the component(s) whose speed DOES NOT remain constant, amongst the following, is/are
- GATE TF - 2024
- Principles of bobbin building in roving formation
View More Questions